1. G?rünü?: gümü? gri metal cilas?
2. Safl?k: W ≥% 99,95
3. Yo?unluk: daha az olmayan 18.3g/cm3
4. Tedarik devlet: sinterleme veya i?leme
5. Kalite standard?: mü?teri g?re
| diameter (mm) | thickness (mm) | height (mm) | Surface finish | inner surface finish | Inner bottom finish |
| 30 ~ 50 | 2 ~ 10 | <500 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 50 ~ 100 | 3 ~ 15 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 100 ~ 150 | 3 ~ 15 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 150 ~ 200 | 5 ~ 20 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 200 ~ 300 | 8 ~ 20 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 300 ~ 400 | 8 ~ 30 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 400 ~ 450 | 8 ~ 30 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
| 450 ~ 600 | 8 ~ 30 | <1000 | <Ra2.0 | <Ra2.4 | <Ra2.8 |
?zel boyut mü?terilerin ihtiya?lar?na g?re imal edilebilir
hammadde (tungsten tozu) --- izostatik presleme --- mekanik i?leme --- indüksiyon sinterleme E?ER --- mekanik i?leme-alg?lama onay --- tungsten potalar?
CNC dikey torna makinesi, CNC freze, tel kesme makinesi
Tungsten erime noktas? 3380 oC ula?t???ndan, tungsten pota yayg?n tür safir büyüme f?r?n?, kuvars cam eritme f?r?n? ve nadir toprak eritme oca?? gibi endüstri f?r?n?nda uygulan?r. Tungsten pota ortamda ?al??ma s?cakl??? 2000 ° C'nin üzerinde oldu?u Safir kristal büyüme f?r?n, yüksek safl?kta, yüksek yo?unluklu, kesin ?l?üm ve pürüzsüz yüzeyi, di?er ?zellikleri ile hi?bir i?-?atlak tungsten pota belirleyici tohum büyüme ba?ar? oran? üzerindeki etkisi ?ekerek kristal kalite kontrol, metamiktizasyon pot kararl? ve vard?r i?in hizmet safir büyüme sürecinde ya?am ve biz profesyonel birimler taraf?ndan kontrol edilmesi i?in haz?r?z.